Up to now, green synthesis of "naked" nanoobjects with clean surfaces is still a great challenge since structure-directing agents such as surfactants are usually used to induce the anisotropic particle growth for interesting nanostructures in solution. Here, a green synthesis approach for preparing "naked" Pt nanoparticles (NPs) in acetic acid solution was reported. Interestingly, Pt NPs with different morphologies (well-defined polyhedrons, irregular polyhedron-constructed chain networks and nanoflower-constructed chain networks) could be successfully synthesized at different concentrations of acetic acid without adding additional structure-directing agents and reducing agents. The acetic acid itself works both as structure-directing agent and reducing agent for the formation of these interesting Pt NPs. Specifically; the synthesized NPs are "naked" with clean surfaces since the acetic acid is a weakly-capping agent which can be easily removed after the washing process. The versatility of this method is further demonstrated by preparation of "naked" PtPd alloy NPs. In particular, the as-prepared "naked"Pt_ (5.20) and Pt3Pd1_ (5.20) NPs are demonstrated to be excellent catalysts with much higher electroactivity and better durability than the commercial Pt black catalyst (Hispec (TM) 1000) for the methanol oxidation reaction. The method reported in this work may pave the way for simple, low-cost, green and eco-friendly synthesis of "naked" metal catalysts for advanced electrocatalytic applications.
- 出版日期2016
- 单位山东大学