Composites of a Prussian Blue Analogue and Gelatin-Derived Nitrogen-Doped Carbon-Supported Porous Spinel Oxides as Electrocatalysts for a Zn-Air Battery

作者：Lee Jang Soo; Nam Gyutae; Sun Jie; Higashi Shougo; Lee Hyun Wook; Lee Sanghan; Chen Wei; Cui Yi^*; Cho Jaephil^*

来源：Advanced Energy Materials, 2016, 6(22): 1601052.

DOI：10.1002/aenm.201601052

• gelatin
• mass transfer
• oxygen reduction reaction
• Prussian blue analogue
• Zn-air batteries

To date, most studies have focused only on the interaction between oxygen and the catalyst, with the intention of minimizing the mass-transfer resistance by using the rotating disk electrode (RDE) method, which is based on the forced-convection theory. To begin with, in order to increase the reaction rate, the oxygen should be able to reach the active sites of the catalyst readily (mass transfer). Next, a moderate (i.e., not too strong or weak) interaction (kinetics) should be maintained between the oxygen molecules and the catalyst, in order to allow for better adsorption and desorption. Therefore, these two factors should be taken into consideration when designing electrocatalysts for oxygen reduction. Further, there is bound to be a demand for large-scale metal-air batteries in the future. With these goals in mind, in this study, a facile and scalable method is developed for fabricating metal-air batteries based on the fact that the Prussian blue analogue Mn-3[Co(CN)(6)](2)center dot nH(2)O and gelatin-coated Ketjenblack carbon thermally decompose at 400 degrees C in air (i.e., without requiring high-temperature pyrolysis under inert conditions) to form porous spinel oxides and N-doped carbon materials. The intrinsic kinetics characteristics and the overall performance of the resulting catalysts are evaluated using the RDE method and a Zn-air full cell, respectively.

• 出版日期2016-11-23