Mg-Cu-Zn ultrafine eutectic composites with different length scale heterogeneity, consisting of micrometer size dendrites and/or ultrafine scale bimodal eutectics, exhibit high yield strength as well as good plasticity at room temperature compression. Among these alloys, micron-scale alpha-Mg dendrites reinforced ultrafine eutectic composites exhibit high yield strength of 310 similar to 420 MPa and large plasticity of 7 similar to 12%. Meanwhile, a Mg(72)Cu(5)Zn(23) alloy comprising a bimodal eutectic structure without the micron-scale alpha-Mg dendrites shows the optimized mechanical properties the highest yield strength of 455 MPa combined with a considerable plastic strain of similar to 5%.