Anti-irradiation performance against helium bombardment. in bulk metallic glass (Cu47Zr45Al8)(98.5)Y-1.5

作者：Mei, Xianxiu^*; Wang, Bin; Dong, Chuang; Gong, Faquan; Wang, Younian; Wang, Zhiguang

来源：Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms , 2013, 307: 11-15.

DOI：10.1016/j.nimb.2012.12.070

• He2+ ion irradiation
• Metallic glass
• Polycrystal W
• Irradiation damage

In order to compare the resistance to He2+ ion induced irradiation between metallic glass and polycrystal W metal, this paper used different fluences of He2+ ion-irradiated metallic glass (Cu47Zr45Al8)(98.5)Y-1.5 and polycrystal W with an energy of 500 keV. The SRIM simulation calculation results showed that the range (1.19 mu n) of He2+ in metallic glass was greater than the one (0.76 mu m) in polycrystal W. The SEM analysis showed that there was no significant irradiation damage phenomenon on the surface of metallic glass, and there was only a damage layer 1.45 mu m away from the surface when the fluence reached 2 x 10(18) ions/cm(2). For W, there were surface peeling, flaking and other surface damages at a fluence of 1 x 10(18) ions/cm(2); when the fluence increased to 2 x 10(18) ions/cm(2), multilayer detachment phenomenon appeared. The surface root mean square roughness of metallic glass (Cu47Zr45Al8)(98.5)Y-1.5 first increased and then decreased with the increase of fluence. The surface reflectivity of (Cu47Zr45Al8)(98.5)Y-1.5 decreased with the increase of fluence. Through detection by XRD, it was found that (Cu47Zr45Al8)(98.5)Y-1.5 always maintained amorphous phase after different fluences of radiation. The resistance to He2+ irradiation of metallic glass (Cu47Zr45Al8)(98.5)Y-1.5 was superior to the one in polycrystal W.

• 出版日期2013-7-15
• 单位中国科学院近代物理研究所; 大连理工大学