We developed a very simple and new joint technique for coated conductors that could achieve a very low resistance less than 0.02 mu Omega across the joint with an area of 2 x 20 mm(2) without any degradation of I-c. It is a diffusion joint using the Ag stabilizing layer of YBCO coated conductors. Two tapes were stuck with Ag stabilizing layer in contact in a face to face manner and were pressed uniaxially during a heat treatment from 500 degrees C to room temperature in a pure oxygen atmosphere. The relationship between the joint pressure, the joint structure and I-c were studied.
- 出版日期2006-10-1