A novel solution method for selective synthesis of pure t-LaVO4

作者：Xie, Baogeng; Lu, Guanzhong^*; Wang, Yanqin; Guo, Yun; Guo, Yanglong

来源：Materials Letters, 2011, 65(2): 240-243.

DOI：10.1016/j.matlet.2010.09.079

• Crystal structure
• Luminescence
• Nanomaterials
• Hydrothermal synthesis

Tetragonal phase LaVO4 (t-LaVO4) was successfully selectively synthesized through a simple solution method with La(NO3)(3) and NaVO4 as starting materials without any templates or catalysts. The products were characterized by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). XRD patterns showed that pure t-LaVO4 could be obtained in wide ranges of pH value and crystallization temperature. TEM images revealed that nanorods with different aspect ratios were obtained in different synthesis conditions. The shorter nanorods had mean diameters of about 18-25 nm and lengths of 40-60 nm. However, the longer nanorods had uniform sizes with an average aspect ratio about 10. It was interesting to discover that t-LaVO4 could be formed even at room temperature (RT), which might be beneficial for a large scale production. Different luminescence performances of the samples doped 5% Eu3+ were also investigated.

• 出版日期2011-1-31
• 单位华东理工大学