Adsorption Forms of CO2 on MIL-53(Al) and NH2-MIL-53(Al) As Revealed by FTIR Spectroscopy

作者：Mihaylov Mihail; Chakarova Kristina; Andonova Stanislava; Drenchev Nikola; Ivanova Elena; Sabetghadam Anahid; Seoane Beatriz; Gascon Jorge; Kapteijn Freek; Hadjiivanov Konstantin^*

来源：Journal of Physical Chemistry C, 2016, 120(41): 23584-23595.

DOI：10.1021/acsjpcc.6b07492

Adsorption of CO2 on MIL-53(Al) and NH2MIL-53(AI) has been studied by Fourier transform infrared (FTIR) spectroscopy at different temperatures and equilibrium pressures. For better interpretation of the spectra (CO2)-C-13 was also utilized. It is established that with both samples at low coverages CO2 forms O-bonded complexes with the structural OH groups (OH center dot center dot center dot(OCO)-C-12). These species are characterized by v(3)((CO2)-C-12) at 2337-2338 cm(-1) and two v(2)((CO2)-C-12) modes around 662 and 650 cm(-1). Simultaneously, the v(OH) modes of the hydroxyl groups are red-shifted, while the delta(OH) modes are blue-shifted. At higher coverages (OH center dot center dot center dot(OCO)-C-12)(2) dimeric species are formed and this leads to a decrease of the v(3)(CO2) frequency by 2-4 cm(-1). This change is due to vibrational interaction as proven by the observation that the frequency remains practically unaffected for (OH center dot center dot center dot(OCO)-C-12) (OH-(OCO)-C-13) dimeric species. Interaction between dimers leads to additional slight decrease of the value of v(3)(CO2). In parallel with the CO2 adsorption a partial transformation of the material from large pore to narrow-pore form occurs. Far before CO2 interacts with all hydroxyl groups, polymeric CO2 species are produced within the MIL-53(Al) sample. They are characterized by a split v(3)(CO2) mode with a pronounced component at 2340 cm(-1). The formation of these species involves some of the dimers and is accompanied by a reopening of the MIL-53 structure. Analysis of the shift of the OH modes led to the conclusion that the polymeric moiety interacts strongly with one OH group and more weakly with several other hydroxyls. No polymeric species were observed with the NH2-MIL-53(A1) sample which is associated with the more stable narrow-pore structure of this material. However, evidence of interaction between CO2 and the hydroxyls H bonded to amino groups was found.

• 出版日期2016-10-20