A-type zeolite containing Ag+/Zn2+ as inorganic antifungal for waterborne coating formulations

作者：Pereyra Andrea M^*; Gonzalez Maximiliano R; Rosato Vilma G; Basaldella Elena I

来源：Progress in Organic Coatings, 2014, 77(1): 213-218.

DOI：10.1016/j.porgcoat.2013.09.008

• A-type zeolite
• Inorganic biocides
• Waterborne coating
• Aspergillus niger

The biocide cations Ag+ and Zn2+ were hosted in the cavities of an ordered aluminosiliceous framework. Starting from sodium A-type zeolite (NaA), LTA containing Ag+ (AgA), Zn2+ (ZnA) and Ag+/Zn+ (AgZnA) at different cation exchanged levels was obtained and its antifungal properties were evaluated. To determine the minimum inhibitory concentration (MIC) of the exchanged zeolites against Aspergillus niger, [Ag+] and [Zn2+] values ranging from 50 < [Ag+] < 1000 mg L-1 to 650 < [Zn2+] < 2000 mg L-1, respectively, were used for NaA, and for AgZnA: 30 < Ag+ < 250 mg L-1. The zeolite sample having [Ag+] = 100 mg L-1, [Zn2+] = 90 mg L-1 produces a growth inhibition comparable to that achieved with 230 mg L-1 of Ag+1 (MIC value obtained for the single cation). The antifungal activity of these products after incorporation in waterborne coating formulations was also determined. Results indicate that Ag+ and Zn2+ supported on A-type zeolite could be a beneficial tool for the development of waterborne coatings with a longer protection against microbiological attack when compared to traditional organic biocides.

• 出版日期2014-1