A 3D Co-CN framework as a high performance electrocatalyst for the hydrogen evolution reaction

作者：Chen, Jie; Zhou, Haifeng; Huang, Yongjun; Yu, Huiwu; Huang, Fuying; Zheng, Fengying; Li, Shunxing^*

来源：RSC Advances, 2016, 6(48): 42014-42018.

DOI：10.1039/c6ra05632f

• EFFICIENT ELECTROCATALYSTS
• HOLLOW SPHERES
• CARBON CLOTH
• MOS2
• NANOPARTICLES
• NANOTUBES
• GRAPHENE
• NANOSHEETS
• PHOSPHIDE
• CATALYSTS

A 3D Co-CN framework was synthesized via a sample annealing route at 600 degrees C using ZIF-67 as the template. When the 3D framework was applied as a hydrogen evolution cathode, the Co-CN electrode shows exceptionally high catalytic activity and good durability, and it only requires overpotentials of 181 mV and 266 mV to afford current densities of 10 mA cm(-2) in acid (0.5 M H2SO4) and alkaline (0.1 M KOH) electrolytes respectively.