Development of a new alluaudite-based cathode material with high power and long cyclability for application in Na ion batteries in real-life

作者：Kim Jongsoon^*; Kim Hyungsub; Lee Seongsu; Myung Seung Taek

来源：Journal of Materials Chemistry A, 2017, 5(42): 22334-22340.

DOI：10.1039/c7ta06693g

We report Na2Fe1.96V0.96(PO4)(3) (NFVP) as a new cathode material for Na ion batteries with outstanding cycle life and high power density for the first time. Structural characterization of NFVP was performed using Rietveld refinement of X-ray diffraction and neutron diffraction patterns, which revealed large Na diffusion paths in the structure that enabled rapid Na (de) intercalation without a large volume change. Using X-ray diffraction and X-ray photoelectron spectroscopy with charge/discharge measurements, it was confirmed that based on redox reactions of Fe and V ions, similar to 2 Na ions are reversibly (de) intercalated from the structure with an average voltage of similar to 3.1 V (vs. Na+/Na). At 30C, which denotes the rapid charge/discharge, similar to 74% of the theoretical capacity was delivered. Furthermore, NFVP exhibited an outstanding cycle life of over 2500 cycles (similar to 70% retention of the initial capacity), which can be attributed to the low volume change (similar to 1%) during charge/discharge.

• 出版日期2017-11-14