摘要
Electron backscatter diffraction has been increasingly used to identify the crystallographic planes and orientation of cleavage facets with respect to the rolling direction in fracture surfaces. The crystallographic indices of cleavage planes can be determined either directly from the fracture surface or indirectly from metallographic sections perpendicular to the plane of the fracture surface. A combination of electron backscatter diffraction and 3D scanning electron microscopy imaging technique has been modified to determine crystallographic facet orientations. The main purpose of this work has been to identify the macroscopic crystallographic orientations of cleavage facets in the fracture surfaces of weld heat affected zones in a well-known steel fractured at low temperatures. The material used for the work was an American Petroleum Institute (API) X80 grade steel developed for applications at low temperatures, and typical heat affected zone microstructures were obtained by carrying out weld thermal simulation. The fracture toughness was measured at different temperatures (0 degrees C, -30 degrees C, -60 degrees C and -90 degrees C) by using Crack Tip Opening Displacement testing. Fracture surfaces and changes in microstructure were analyzed by scanning electron microscopy and light microscopy. Crystallographic orientations were identified by electron backscatter diffraction, indirectly from a polished section perpendicular to the major fracture surface of the samples. Computer assisted 3D imaging was used to measure the angles between the cleavage facets and the adjacent polished surface, and then these angles were combined with electron backscatter diffraction measurements to determine the macroscopic crystallographic planes of the facets. The crystallographic indices of the macroscopic cleavage facet planes were identified to be {100}, {110}, {211} and {310} at all temperatures.
- 出版日期2013-7