Anomalous deformation twinning in coarse-grained Cu in Ag60Cu40 composites under high strain-rate compressive loading

作者：Eftink B P^*; Mara N A; Kingstedt O T; Safarik D J; Lambros J; Robertson I M

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2014, 618: 254-261.

DOI：10.1016/j.msea.2014.08.082

• Twinning
• Copper
• Silver
• Slip

The deformation response of a directionally solidified Ag60Cu40 eutectic alloy with a cube-on-cube orientation relationship between Ag and Cu subjected to high strain-rate 10(3) s(-1) compressive loading was examined. Loading at 45 degrees and 90 degrees to the growth axis, near [001] and [11 (1) over bar] local crystal orientations, respectively, resulted in deformation twinning and dislocation slip in both Ag and Cu under conditions where deformation twinning would not normally be expected in Cu. In contrast, loading at 0 degrees and 90 degrees to the growth axis, near < 101 > local crystal orientations, resulted in the primary deformation mode being dislocation slip. These results are interpreted in terms of the influence of loading axis with respect to the local crystal orientation in the directionally solidified alloy and on slip transmission from Ag into Cu.

• 出版日期2014-11-17
• 单位Los Alamos