Novel preparation and near-infrared photoluminescence of uniform core-shell silver sulfide nanoparticle@mesoporous silica nanospheres

作者：Han Lu; Lv Yingying; Asiri Abdullah M; Al Youbi Abdulrahman O; Tu Bo^*; Zhao Dongyuan

来源：Journal of Materials Chemistry, 2012, 22(15): 7274-7279.

DOI：10.1039/c2jm16168k

In this paper, we report a facile one-pot route to prepare core-shell Ag2S@MSN mesoporous silica nanospheres with near-infrared (NIR) photoluminescent properties. The Ag2S@MSN nanospheres have uniform core-shell structures with single monoclinic alpha-Ag2S nanocrystal core (similar to 17 nm), ordered mesoporous silica shell (the thickness of similar to 20 nm), very high surface area (similar to 909 m(2) g(-1)), and uniform pore size (similar to 2.6 nm). The core-shell Ag2S@MSN nanospheres show NIR emission at around 1275 nm excited by a 648 nm laser diode, which can be observed in a wide range of concentration (0.2 similar to 3.2 mg mL(-1)). The stability of the NIR photoluminescence for the core-shell Ag2S@MSN nanospheres is greatly improved compared to the bare Ag2S nanocrystals. The NIR emission intensity could be enhanced after the hydrothermal treatment with the increase of crystallinity of the silver sulfide cores. The thickness of mesoporous silica shell could be tuned by adjusting the amount of silica source. Furthermore, the core-shell Ag2S@MSN nanocomposites with several small Ag2S nanoparticles in one mesoporous silica shell could also be obtained, which may be a good candidate for bioimaging and biolabeling.

• 出版日期2012
• 单位复旦大学