Size-controlled synthesis of Pt nanoparticles and their electrochemical activities toward oxygen reduction

作者：Kim Joung Woon; Lim Borami; Jang Hyun Sook; Hwang Seung Jun; Yoo Sung Jong; Ha Jeong Soo; Cho Eun Ae; Lim Tae Hoon; Nam Suk Woo; Kim Soo Kil^*

来源：International Journal of Hydrogen Energy, 2011, 36(1): 706-712.

DOI：10.1016/j.ijhydene.2010.09.055

• PEMFC
• Pt catalyst
• Size control
• Oxygen reduction

Pt/C catalysts with high activity toward oxygen reduction reactions are fabricated in the presence of FeCl(3) as an additive to control the Pt particle size. The polyol method is used for fabrication; 20 wt% Pt/C catalysts are produced with various amounts of FeCl(3) under different fabrication conditions such as pH and temperature. Adding FeCl(3) significantly reduces Pt particle size, which is believed to occur as a result of the interference of Pt reduction rate by Fe(3+) ions. The average Pt particle size obtained using the fabrication conditions of Pt:Fe = 1:3 (mole ratio), pH = 10, and 130 degrees C is around 2.0 nm, which is much smaller than that of commercial or homemade Pt/C produced in the absence of FeCl(3). The electrochemically active surface area of this catalyst is 60.6 m(2)/g. The mass activities at 0.9 and 0.85 V are 15.3 and 42.7 mA/mg(Pt), respectively, which is about 1.8-2.1 times higher than those of commercial Pt/C catalysts. PEMFC test results show that the performance of the Pt/C catalyst fabricated with FeCl(3) additive is better than that of as commercial catalyst.

• 出版日期2011-1