Nanocontact Electrification through Forced Delamination of Dielectric Interfaces

作者：Cole Jesse J; Barry Chad R; Wang Xinyu; Jacobs Heiko O^*

来源：ACS Nano, 2010, 4(12): 7492-7498.

DOI：10.1021/nn1016692

• nanocontact electrification
• transfer printing
• nanoxerography
• flexible printable electronics
• charge patterning

This article reports patterned transfer of charge between conformal material Interfaces through a concept referred to as nanocontact electrification. Nanocontacts of different size and shape are formed between surface-functionalized polydimethylsiloxane (PDMS) stamps and other dielectric materials (PMMA, SiO(2)). Forced delamination and cleavage of the Interface yields a well-defined charge pattern with a minimal feature size of 100 nm. The process produces charged surfaces and associated fields that exceed the breakdown strength of air, leading to strong long-range adhesive forces and force distance curves, which are recorded over macroscopic distances. The process is applied to fabricate charge-patterned surfaces for nanoxerography demonstrating 200 nm resolution nanopartide prints and applied to thin film electronics where the patterned charges are used to shift the threshold voltages of underlying transistors.

• 出版日期2010-12