Dehydration process and transient channel deformations of slightly hydrated boron leucite: An "in situ" time-resolved synchrotron powder diffraction study

作者：Martucci A^*; Pecorari P; Cruciani G

来源：Microporous and Mesoporous Materials, 2011, 142(2-3): 570-576.

DOI：10.1016/j.micromeso.2010.12.046

• Borosilicate
• Leucite
• Dehydration
• Rietveld refinement
• In situ X-ray powder diffraction

The step by step thermal dehydration process of slightly hydrated boron leucite K-16[B16Si32O96], was studied in situ by synchrotron radiation powder diffraction. A time-resolved experiment was performed using a translating imaging plate system. Rietveld refinements were carried out on 41 consecutive powder patterns in the 25-940 degrees C temperature range. Results show that temperature-induced transformations can be schematized into two main steps. In the 25-565 degrees C temperature range, the symmetry remained cubic I-43d and the unit cell parameter increased with an increase in temperature. The migration of H2O molecules through the [1 1 1] channels during dehydration determined an opening of the six-member ring apertures which was as wide as possible and, at the same time, a narrowing in the eight-ring along [1 1 1]. This process was accomplished by a twisting in the tetragonal prism, constituting a leucite framework, which led to an opposed tilting in the tetrahedra connecting the prisms. Above 565 degrees C, a continuous structural transformation led to a displacive polymorphic transition. Rietveld structure refinement of the unit cell parameters showed a remarkable change, thus indicating an I-43d -> la-3d change in symmetry. This was associated with a relaxation in the continuous structural distortions of the leucite framework and the T-O-T and O-T-O angles indicated the formation of more regular apertures.

• 出版日期2011-7