Atmospheric corrosion resistance of electroplated Ni/Ni-P/Au electronic contacts

作者：Murugan Vinod K; Jia Zhigang; Syaranamual Govindo J; Gan Chee Lip; Huang Yizhong; Chen Zhong^*

来源：Microelectronics Reliability, 2016, 60: 84-92.

DOI：10.1016/j.microrel.2016.02.014

• Atmospheric corrosion
• Electrodeposition
• Nickel
• Nickel-phosphorus
• Corrosion resistance
• Pitting corrosion

Atmospheric corrosion has vast consequences on the reliability of electronic connectors. This study determined the corrosion resistance of Ni/Ni-P plating metallurgy as a function of plating current density and plating thickness. Discrepancy was observed in the neutral salt spray (NSS) and mixed flowing gas (MFG) tests. Thicker Ni-P deposits displayed superior corrosion resistance in MFG tests while thinner Ni-P deposits performed better in NSS tests. This disparity was attributed to the intrinsic corrosion susceptibility of Ni-P against chlorine or sulfur assisted corrosion. Corrosion products were analysed for better understanding of the corrosion mechanism. NSS test produced green corrosion residues consisting of CuCl (nantokite) and CuCl2(OH)(3) (clinoatacamite) and brown residues consisting of Cu2O (cuprite). MFG test produced sulfides of copper (major) and nickel (minor).

• 出版日期2016-5