Mixed Matrix Carbon Molecular Sieve and Alumina (CMS-Al2O3) Membranes

作者：Song Yingjun; Wang David K; Birkett Greg; Martens Wayde; Duke Mikel C; Smart Simon; da Costa Joao C Diniz^*

来源：Scientific Reports, 2016, 6(1): 30703.

DOI：10.1038/srep30703

This work shows mixed matrix inorganic membranes prepared by the vacuum-assisted impregnation method, where phenolic resin precursors filled the pore of a-alumina substrates. Upon carbonisation, the phenolic resin decomposed into several fragments derived from the backbone of the resin matrix. The final stages of decomposition (>650 degrees C) led to a formation of carbon molecular sieve (CMS) structures, reaching the lowest average pore sizes of similar to 5 angstrom at carbonisation temperatures of 700 degrees C. The combination of vacuum-assisted impregnation and carbonisation led to the formation of mixed matrix of CMS and a-alumina particles (CMS-Al2O3) in a single membrane. These membranes were tested for pervaporative desalination and gave very high water fluxes of up to 25 kg m(-2) h(-1) for seawater (NaCl 3.5 wt%) at 75 degrees C. Salt rejection was also very high varying between 93-99% depending on temperature and feed salt concentration. Interestingly, the water fluxes remained almost constant and were not affected as feed salt concentration increased from 0.3, 1 and 3.5 wt%.

• 出版日期2016-7-29