Densification and polymorphic transition of multiphase Y2O3 nanoparticles during spark plasma sintering

作者：Marder R; Chaim R^*; Chevallier G; Estournes C

来源：Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 2011, 528(24): 7200-7206.

DOI：10.1016/j.msea.2011.06.044

• Spark plasma sintering
• Phase transformation
• Densification
• Y2O3

Multiphase (MP) monoclinic and cubic Y2O3 nanoparticles, 40 nm in diameter, were densified by spark plasma sintering for 5-15 min and100 MPa at 1000 degrees C, 1100 degrees C, and 1500 degrees C. Densification started with pressure increase at room temperature. Densification stagnated during heating compared to the high shrinkage rate in cubic single-phase reference nanopowder. The limited densification of the MP nanopowder originated from the vermicular structure (skeleton) formed during the heating. Interface controlled monoclinic to cubic polymorphic transformation above 980 degrees C led to the formation of large spherical cubic grains within the vermicular matrix. This resulted in the loss of the nanocrystalline character and low final density.

• 出版日期2011-9-15