A Cu(II) formate complex was synthesized by reacting low-cost Cu(II) oxide (CuO) with formic acid. The formate was mixed with alpha-terpineol to prepare a paste, which was stencil printed onto glass slides and thermally annealed under nitrogen at 400 degrees C to fabricate conductive Cu films. The Cu(II) formate decomposed and was transformed into pure Cu particles, which were sintered during annealing. A porous Cu film was obtained because of necking between the Cu particles, and the Cu film annealed for 2 h exhibited an excellent electrical resistivity of 2.13x10(-5) Omega.cm.