A novel triazine-rich polymer wrapped MMT: synthesis, characterization and its application in flame-retardant poly(butylene terephthalate)

作者：Xin, Fei^*; Guo, Chao; Chen, Yu; Zhang, Hailong; Qian, Lijun

来源：RSC Advances, 2017, 7(75): 47324-47331.

DOI：10.1039/c7ra08857d

• MECHANICAL-PROPERTIES
• THERMOPLASTIC POLYESTERS
• THERMAL-DEGRADATION
• NANOCOMPOSITES
• MONTMORILLONITE
• FLAMMABILITY
• MORPHOLOGY
• BEHAVIOR
• PBT
• COMPOSITES

A novel flame retardant (PTAC-MMT) was prepared by wrapping montmorillonite (MMT) with poly(2,4,6triallyloxy-1,3,5-triazine) (TAC) via in situ polymerization, and its structure and properties were characterized by Fourier transformed infrared (FT-IR) spectroscopy, H-1 nuclear magnetic resonance (1H NMR) and C-13 NMR, transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and thermogravimetric analysis (TGA) measurements. The PTAC-MMT and aluminum diethylphosphinate (AlPi) were then incorporated into poly(butylene terephthalate) (PBT) to improve the flame retardancy. The sample containing 1.67 wt% PTAC-MMT and 8.33 wt% AlPi had a LOI value of 36.4% and achieved UL94 V-0 classification. The wrapping flame retardants exhibited excellent anti-dripping effect in PBT composite. This work could provide a novel way to prepare modified MMT and the as-prepared flame retardants.

• 出版日期2017
• 单位北京工商大学