An Al/glass joint created by using ultrasonic welding was analyzed by means of multiscale observation techniques. A cross-sectional analysis of the microstructure revealed that a directly joined interface without reaction phases formed at the periphery of a round joined region. The size of Al grains markedly decreased after ultrasonic welding and some subgrains were observed along the interface. The finer Al grains observed around the periphery of the joined interface showed active plastic flow that promoted welding.