Drain Current Stress-Induced Instability in Amorphous InGaZnO Thin-Film Transistors with Different Active Layer Thicknesses

作者：Wang, Dapeng^*; Zhao, Wenjing; Li, Hua; Furuta, Mamoru^*

来源：Materials, 2018, 11(4): 559.

DOI：10.3390/ma11040559

• drain current stress
• instability
• InGaZnO
• thin-film transistors
• active layer thickness

In this study, the initial electrical properties, positive gate bias stress (PBS), and drain current stress (DCS)-induced instabilities of amorphous indium gallium zinc oxide (a-IGZO) thin-film transistors (TFTs) with various active layer thicknesses (T-IGZO) are investigated. As the TIGZO increased, the turn-on voltage (V-on) decreased, while the subthreshold swing slightly increased. Furthermore, the mobility of over 13 cm(2.)V(-1.)s(-1) and the negligible hysteresis of similar to 0.5 V are obtained in all of the a-IGZO TFTs, regardless of the TIGZO. The PBS results exhibit that the Von shift is aggravated as the TIGZO decreases. In addition, the DCS-induced instability in the a-IGZO TFTs with various TIGZO values is revealed using current-voltage and capacitance-voltage (C-V) measurements. An anomalous hump phenomenon is only observed in the off state of the gate-to-source (C-gs) curve for all of the a-IGZO TFTs. This is due to the impact ionization that occurs near the drain side of the channel and the generated holes that flow towards the source side along the back-channel interface under the lateral electric field, which cause a lowered potential barrier near the source side. As the TIGZO value increased, the hump in the off state of the Cgs curve was gradually weakened.

• 出版日期2018-4
• 单位陕西师范大学