Size-dependent electrocatalytic reduction of nitrite at nanostructured films of hollow polyaniline spheres and polyaniline-polystyrene core-shells

作者：Kazimierska Ewa; Smyth Malcolm R; Killard Anthony J^*

来源：Electrochimica Acta, 2009, 54(28): 7260-7267.

DOI：10.1016/j.electacta.2009.07.039

• Polyaniline
• Nanostructure
• Electrocatalysis
• Nitrite
• Chronocoulometry

Nanostructured films of the conducting polymer polyaniline (PANI) were prepared by its potentiostatic polymerization in the presence of thin polystyrene (PS) nanoparticle templates. Two sizes of PS nanoparticles were used (50 and 100 nm) and electron microscopic analysis showed that core-shell composite films of PANI (PANI-PS(50) and PANI-PS(100)) and, following removal of the PS, hollow structures (PANI(50) and PANI(100)) were formed due to the growth mechanism of PANI around the PS templates. The electrochemical behaviour of the PANI-modified electrodes was studied by cyclic voltammetry, chronocoulometry and amperometry in the presence of nitrite and it was found that nitrite reduction was enhanced by the nanostructuring of the films. The electrocatalys is was dependent on the size of the template, being more pronounced at 50 nm than at 100 nm. The hollow PANI(50) film was also a better catalyst than PANI-PS(50), whereas for structures based on 100 nm templates, the composite film was better. Such behaviour could be explained in terms of larger surface area and surface concentration of PANI(50) and PANI-PS(50) films on the electrodes and by higher differential capacitance of those films.

• 出版日期2009-12-1