Direct Silica-Coating of Quantum Dots

作者：Kobayashi Yoshio^*; Nozawa Takuya; Takeda Motohiro; Ohuchi Noriaki; Kasuya Atsuo

来源：Journal of Chemical Engineering of Japan, 2010, 43(6): 490-493.

• Quantum Dots
• Nanoparticle
• Core-Shell
• Silica-Coating
• Sol-Gel

A method for direct silica-coating of fluorescent semiconductor nanoparticles is proposed. The fluorescent semiconductor nanoparticles used are quantum dots (Q-dots), which are CdSe(x)Te(1-x) nanoparticles coated with ZnS and succeedingly surface-modified with amino groups. The silica-coating was performed in the presence of the Q-dots in 1-15M H(2)O, 0.4 x 10(-4)-40 x 10(-4) M NaOH and 0.5 x 10(-4)-50 x 10(-4) M tetraethyl orthosilicate (TEOS). Silica shells were formed at 5M H(2)O and 4 x 10(-4) M NaOH. Under these concentrations of H(2)O and NaOH, the particle size of silica-coated Q-dots could be varied from 15.8 to 31.7 nm as the TEOS concentration was increased from 2.5 x 10(-4) to 50 x 10(-4) M. The silica-coated Q-dots showed fluorescence as well as the uncoated Q-dots.