This study investigated the high strength of a soy protein adhesive system with good flowability at high protein concentration. Sodium montmorillonite (Na MMT), the most widely used silicate clay, was incorporated into viscous, cohesive soy protein adhesives at concentrations ranging from 1 to 11 % (dry basis, w/w). Hydroxyethyl cellulose was used as a suspension agent to stabilize the soy protein and nano clay to be the dispersion system. The interaction between soy protein and Na MMT was characterized by XRD, FTIR, Zeta potential and DSC. Results indicated that soy protein molecules were adsorbed on the surface of the interlayer of Na MMT through hydrogen bonding and electrostatic interaction. The soy protein/Na MMT adhesives had the intercalation structure with Na MMT contents ranging from 1 to 11 %. Adhesion strength, specifically wet adhesion strength, of soy protein adhesives at isoelectric point (pI) was significantly improved by the addition of Na MMT. It is believed that the physical cross-linking reactions between soy protein and Na MMT mainly contribute to the improved adhesion performance of soy protein adhesives. Wet adhesion strength increased from 2.9 MPa of control soy protein adhesive to 4.3 MPa at 8 % Na MMT. An increase of pH beyond pI value resulted in decreased adhesion strength due to increased surface charges of soy protein and slightly reduced affinity of soy protein on the nano clay surface.
- 出版日期2016-11