摘要

The effects of the annealing methods and annealing temperatures on the pore structures and mechanical properties of porous alumina were investigated. The amorphisation behavior and solidification behavior of the sucrose solutions during annealing were discussed. The pore morphology of porous alumina changed noticeably after uniform annealing. As annealing temperature increased from -25 degrees C to -5 degrees C, the pore morphology of porous alumina changed gradually from irregular lamellar channels to circular channels. After directional annealing, the pore morphology of porous alumina was similar to that after uniform annealing; however, the uniformity of pore channels and the density of pore walls were increased. During directional annealing at -15 degrees C, the compressive strength of porous alumina reached 58.8 MPa, which was 35% higher than that of unannealed porous alumina.