Effect of copper surface pre-treatment on the properties of CVD grown graphene

作者：Kim Min Sik; Woo Jeong Min; Geum Dae Myeong; Rani J R; Jang Jae Hyung^*

来源：AIP Advances, 2014, 4(12): 127107.

DOI：10.1063/1.4903369

Here, we report the synthesis of high quality monolayer graphene on the pre-treated copper (Cu) foil by chemical vapor deposition method. The pre-treatment process, which consists of pre-annealing in a hydrogen ambient, followed by diluted nitric acid etching of Cu foil, helps in removing impurities. These impurities include native copper oxide and rolling lines that act as a nucleation center for multilayer graphene. Raman mapping of our graphene grown on pre-treated Cu foil primarily consisted of similar to 98% a monolayer graphene with as compared to 75 % for the graphene grown on untreated Cu foil. A high hydrogen flow rate during the pre-annealing process resulted in an increased I-2D/IG ratio of graphene up to 3.55. Uniform monolayer graphene was obtained with a I2D/IG ratio and sheet resistance varying from 1.84-3.39 and 1110-1290 Omega/square, respectively.

• 出版日期2014-12