A dye-sensitized solar cell based on low cost nanoscale carbon/TiO(2) composite counter electrode was fabricated and its photovoltaic performance (eta = 5.5%, AM 1.5, 91.5 mW cm(-2)) was comparable to that from platinum counter-electrode devices (eta = 6.4%, AM 1.5, 91.5 mW cm(-2)) made at similar conditions.
- 出版日期2009