Application of calcium phosphates and fibronectin as complementary treatment for osteoporotic bone fractures

作者：Quintana Plaza Javier; Benito Garzon Lorena; Bravo Gimenez Beatriz; Fernandez Montes Moraleda Belen; Collia Francisco; Rodriguez Lorenzo Luis M

来源：Injury-International Journal of the Care of the Injured, 2016, 47: S15-S21.

DOI：10.1016/s0020-1383(16)30601-5

• Osteoporotic
• Fibronectin
• Hydroxyapatite
• Osteosynthesis

Introduction: The gradual aging of the population results in increased incidence of osteoporotic bone fractures. In a good quality bone, the fixation with the usual methods is adequate, but not in osteoporotic bone, in which consolidation delays and other complications are common, with failure rates for screws up to 25%.
Objective: To test fibronectin loaded hydroxyapatite as a complementary treatment for osteoporotic fractures.
Material and Methods: This study was performed in a vivo model; 42 female osteoporotic adult rabbits 4-5 kg (White New Zealand) were used. Two groups (hydroxyapatite and fibronectin loaded hydroxyapatite) and a control group were tested. 3 time points 24 h, 48 h and 5 days were studied. Defects were created in both femurs, in one of them, a cannulated screw (4 mm) and a biocompatible material were placed; in the other femur a screw was inserted without supplemented material forming the control group. Osteoporosis was induced from models already known throughout administration of steroids. Samples were analyzed histologically and through imaging (micro Ct).
Results: Basal levels of BMD are observed belowto normal when compared to other studies (0.25/0.3 instead of 0.4). Global and dependent of time analysis of samples, show no significant differences for samples analyzed. However, an important trend was noted for variables that define the trabecular bone microarchitecture. Indices that define trabecular microarchitecture in the comparative analysis found to have statistical differences (p < 0.01).
Discussion: Osteosynthesis in an osteoporotic bone is a challenge for the surgeon, due to a reduced bone mineral density and different bone architecture. The main finding was the verification of the hypothesis that the trabecular bone parameters increases with our augmentation material in weak rabbit bone quality. Also, the histological analyses of samples show an increase of non inflammatory cells in protein samples (OHAp-Fn) from the first 24 hours.
Conclusion: An early response of rabbit osteroporotic bone to a complementary treatment with fibronectin loaded hydroxyapatite has been observed. This response is reflected in greater values for indices that define the trabecular bone microarchitecture, thickness and separation, a greater non-inflammatory cellularity after only 24 hours and an increased amount of connective tissue observed at 48 hours.