A single crystal X-ray and powder neutron diffraction study on NASICON-type Li1+xAlxTi2-x(PO4)(3) (0 <= x <= 0.5) crystals: Implications on ionic conductivity

作者：Redhammer G J^*; Rettenwander D; Pristat S; Dashjav E; Kumar C M N; Topa D; Tietz F

来源：Solid State Sciences, 2016, 60: 99-107.

DOI：10.1016/j.solidstatesciences.2016.08.011

• LiTi2(PO4)(3)
• Al3+ substitution
• LATP
• NASICON
• Single crystal X-ray diffraction
• Neutron diffraction

Single crystals of NASICON-type material Li1+xTi2-xAlx(FO4)(3) (LATP) with 0 <= x <= 0.5 were successfully grown using long-term sintering techniques. Sample material was studied by chemical analysis, single crystal X-ray and neutron diffraction. The Ti4+ replacement scales very well with the Al3+ and Li+ incorporation. The additional Li+ thereby enters the M3 cavity of the NASICON framework at x, y, z similar to (0.07, 0.34, 0.09) and is regarded to be responsible for the enhanced Li+ conduction of LATP as compared to Al-free LTP. Variations in structural parameters, associated with the Ti4+ substitution with Al3+ + Li+ will be discussed in detail in this paper.

• 出版日期2016-10
• 单位MIT