Lu3Al5O12:Ce@SiO2 phosphor-in-glass: Its facile synthesis, reduced thermal/chemical degradation and application in high-power white LEDs

作者：Xu, Jian^*; Hassan, Dhia A.; Zeng, Ren-Jie; Peng, Dong-Liang

来源：Journal of the European Ceramic Society, 2016, 36(8): 2017-2025.

DOI：10.1016/j.jeurceramsoc.2016.01.007

• Luminescence
• Thermal degradation
• Phosphor-in-glass
• SiO2 coating
• LuAG:Ce

Phosphor-in-glass (PiG) approach draws great attention because polymer encapsulants can be avoided during the wLEDs fabrication. However, phosphor degradation occurs, primarily in co-sintering process (with glass) which significantly reduces the emission intensity of the PiG. The aim of the present study is to develop a thermally/chemically robust color converter. Lu3Al5O12:Ce@SiO(2)core-shell structure was proposed to reduce phosphor degradation during the PiG fabrication. Uniform SiO2 shell with tunable thickness was obtained via a facile process. For the PiG samples sintered at 680 degrees C for 30 min, internal QE of the Lu3Al5O12:Ce@SiO2 based PiG retained 59% of the initial value which was obviously higher than that of the pristine Lu3Al5O12:Ce based PiG (48%). A high-power wLED was constructed by coupling the PiG plate with a 440 nm InGaN blue chip. Under a driving current of 500 mA, the device showed a luminous efficacy of 1291m/W.

• 出版日期2016-7
• 单位厦门大学