A hybrid cobalt disulfonate with a novel inorganic layer architecture exhibiting a field-induced magnetic transition

作者：Feller Russell K; Melot Brent C; Forster Paul M; Cheetham Anthony K^*

来源：Journal of Materials Chemistry, 2009, 19(17): 2604-2609.

DOI：10.1039/b816815f

We report the synthesis, crystal structure, and magnetic properties of Co(3)(OH)(4)(ethanedisulfonate), a layered cobalt hydroxide pillared by ethanedisulfonate ligands (P2(1)/c, a = 8.9462(6) angstrom, b = 5.2818(4) angstrom , c = 10.1259(7) angstrom, beta = 93.297(2)degrees, V = 477.68(6) angstrom(3), Z = 2). The structure displays two-dimensional infinite Co-O-Co connectivity, with the octahedra forming what we believe is a novel M(3)X(8) inorganic layer topology; brucite-like ribbons of edge-sharing octahedra share corners with other ribbons along a second direction to form perforated layers of octahedra. Magnetic measurements reveal a sharp peak in susceptibility at 38 K, with a Curie-Weiss constant of -243 K and an effective magnetic moment (mu(eff)) of 4.35 mu(B) per Co. A field-induced transition from a triangular antiferromagnetic to a collinear ferrimagnetic state occurs in high fields. Heat capacity measurements indicate a relatively small magnetic entropy change, suggesting that the magnetic ordering is only two-dimensional. Thermogravimetric analysis and differential thermal analysis of the material show stability to 350 degrees C.

• 出版日期2009