High-temperature performance of mortars and concretes based on alkali-activated slag/metakaolin blends

作者：Bernal S A^*; Mejia de Gutierrez R; Ruiz F; Quinones H; Provis J L

来源：Materiales de Construccion, 2012, 62(308): 471-488.

DOI：10.3989/mc.2012.01712

• alkali-activated binders
• high temperatures
• granulated blast-furnace slag
• metakaolin
• mechanical properties

This paper assesses the performance of mortars and concretes based on alkali activated granulated blast-furnace slag (GBFS)/metakaolin (MK) blends when exposed to high temperatures. High stability of mortars with contents of MK up to 60 wt.% when exposed to 600 degrees C is identified, with residual strengths of 20 MPa following exposure to this temperature. On the other hand, exposure to higher temperatures leads to cracking of the concretes, as a consequence of the high shrinkage of the binder matrix and the restraining effects of the aggregate, especially in those specimens with binders containing high MK content. A significant difference is identified between the water absorption properties of mortars and concretes, and this is able to be correlated with divergences in their performance after exposure to high temperatures. This indicates that the performance at high temperatures of alkali-activated mortars is not completely transferable to concrete, because the systems differ in permeability. The differences in the thermal expansion coefficients between the binder matrix and the coarse aggregates contribute to the macrocracking of the material, and the consequent reduction of mechanical properties.

• 出版日期2012