Nanostructurization of Nb by high-pressure torsion in liquid nitrogen and the thermal stability of the structure obtained

作者：Popov V V^*; Popova E N; Stolbovskii A V; Pilyugin V P; Arkhipova N K

来源：Physics of Metals and Metallography, 2012, 113(3): 295-301.

DOI：10.1134/S0031918X1203009X

• nanocrystalline structure
• thermal stability
• high-pressure torsion
• electron microscopy
• microhardness

The evolution of the Nb structure upon high-pressure torsion (HPT) in a Bridgeman chamber in liquid nitrogen and a subsequent annealing in the range from 100 to 600A degrees C has been studied by the TEM method. With an increase in the degree of deformation, the structure exhibits three stages of refinement: dislocation cellular structure; mixed structure consisting of cells and subgrains; and submicron or nanocrystalline grain structure. The HPT using 3 and more revolutions of the anvils at 80 K leads to the formation in Nb of a nanocrystalline structure with an average grain size of similar to 75 nm and a record high microhardness of 4800 MPa. The structure is stable at room temperature but possesses a relatively low thermal stability, i.e., the recrystallization starts at lower temperatures than it does after conventional deformation or an HPT at room temperature.

• 出版日期2012-3