A comparative study of photoconductivity and carrier transport in a-Si:H p-i-n solar cells with different back contacts

作者：Kaplan R^*; Kaplan B; Hegedus S S

来源：Solid-State Electronics, 2010, 54(1): 22-27.

DOI：10.1016/j.sse.2009.09.008

• a-Si:H p-i-n solar cells
• Back reflectors
• Photocurrent
• Quantum efficiency
• Recombination
• Trapping

Effects of different back contacts (Al, Cr, ZnO/Ag, Ag) have been measured on hydrogenated amorphous silicon (a-Si:H) p-i-n solar cell performances and are interpreted in terms of changing recombination kinetics. Dc and frequency-resolved photocurrent measurements in a-Si:H p-i-n solar cells have been carried out experimentally. In particular, the J-V characteristics in the dark and light, the external quantum efficiency spectra, the intensity-, temperature-, bias voltage- and frequency-dependence of photocurrent were obtained. Fill factor (FF) values were determined from J-V characteristics for p-i-n cells with different back contacts under various illumination levels. The exponent nu in the power-law relationship, I-ph alpha G(nu), between generating flux density and photocurrent were determined at different bias voltages (dc) and modulation frequencies. The activation energies were obtained from the temperature-dependence of photocurrent measurements. The integrated external quantum efficiencies were calculated from the spectral photoresponse distributions under reverse bias conditions. The modulation-frequency effects on spectral distributions were also investigated. The results were compared for all cells which have different back contacts and excitation intensity.

• 出版日期2010-1