Design and growth of dendritic Cu2-xSe and bunchy CuSe hierarchical crystalline aggregations

作者：Li, Dapeng; Zheng, Zhi^*; Lei, Yan; Ge, Suxiang; Zhang, Yidong; Zhang, Yange; Wong, Ka Wai; Yang, Fengling; Lau, Woon Ming

来源：CrystEngComm, 2010, 12(6): 1856-1861.

DOI：10.1039/b919087m

• CHEMICAL BATH DEPOSITION
• SELENIDE THIN-FILMS
• ROOM-TEMPERATURE
• SOLAR-CELLS
• SE
• ROUTE
• NANOPARTICLES
• MORPHOLOGIES
• EVOLUTION
• SILVER

Dendritic nanocrystals of copper selenide were fabricated in situ for the first time by using alcohol as the solvent. Cu2-xSe films composed of hierarchically ordered dendritic nanostructures were prepared on Cu substrates at a rather moderate temperature of 190-200 degrees C for just 1-3 h, while bunchy CuSe nanostructures could be further constructed above the Cu2-xSe dendrites by prolonging the reaction time of solvothermal growth with ethanol as the solvent. The resulting Cu2-xSe nanodendrites display highly symmetric corolitic morphology while the bunchy CuSe aggregations show particular nanostructures with a pronounced trunk and actinomorphic multi-branches. It is also found that the dendritic structures of crystalline Cu2-xSe could never be obtained when the reaction temperature is less than 190 degrees C, while the temperature needed is 160 degrees C for Ag2Se nanodendrites and higher than 220 degrees C for CdSe nanodendrites. These copper selenide nanostructures with hierarchically ordered 3-dimensional (3D) framework exhibited good absorbance and photoluminescence (PL) property and could bear potential applications in solar cell devices in the future.

• 出版日期2010
• 单位许昌学院; 华中师范大学