Among the recent investigations on transparent electrode materials applied in photoelectric devices, poly(3,4-ethylenedioxythiophene): polystyrene sulfonate (PEDOT: PSS) has been widely used because of its high transparency and low material cost. However, its relatively low conductivity, hygroscopicity, and acidity limit its further application. Herein, a novel PEDOT: PSS: S-AgNWs composite has been prepared via the in situ oxidative polymerization of EDOT using PSS and 4-mercaptobenzenesulfonic acid-modified silver nanowires (S-AgNWs), in which there are electrostatic interactions between PEDOT and sulfonic groups from PSS and S-AgNWs. When compared with commercial Clevios PH1000, a more crystalline and conductive PEDOT with quinoid conformation was developed by partially substituting PSS with the S-AgNWs; this resulted in the formation of PEDOT: PSS: S-AgNWs showing a lower sheet resistance (64 Omega sq(-1) at similar to 94.8% transmittance). Furthermore, due to reduced work function, hygroscopicity, and acidic properties of PEDOT: PSS: S-AgNWs derived from the in situ composite between S-AgNWs and PEDOT, as well as the reduction in the PSS content, PEDOT: PSS: S-AgNWs was used as a transparent electrode for the formation of organic solar cells (OSCs), displaying a power conversion efficiency of 10.2% and good storage stability.