A Nonchlorinated Solvent-Processable Fluorinated Planar Conjugated Polymer for Flexible Field-Effect Transistors

作者：Lee Myeongjae; Kim Min Je; Ro Suhee; Choi Shinyoung; Jin Seon Mi; Nguyen Hieu Dinh; Yang Jeehye; Lee Kyung Koo; Lim Dong Un; Lee Eunji; Kang Moon Sung; Choi Jong Ho; Cho Jeong Ho^*; Kim BongSoo^*

来源：ACS Applied Materials & Interfaces, 2017, 9(34): 28817-28827.

DOI：10.1021/acsami.7b08071

• organic transistor
• nonchlorinated solvent
• low bandgap polymer
• carrier mobility
• flexible electronics
• mechanical stability

High carrier mobilities have recently been achieved in polymer field effect transistors (FETs). However, many of these polymer FET devices require the use of chlorinated solvents such as chloroform (CF), chlorobenzene (CB), and odichlorobenzene (DCB) during fabrication. The use of these solvents is highly restricted in industry because of health and environmental issues. Here, we report the synthesis of a low band gap (1.43 eV, 870 nm) semiconducting polymer (PDPP2DT-F2T2) having a planar geometry, which can be readily processable with nonchlorinated solvents such as toluene (TOL), o-xylene (XY), and 1,2,4-trimethylbenzene (TMB). We performed structural characterization of PDPP2DT-F2T2 films prepared from different solvents, and the electrical properties of the films were measured in the context of FETs. The devices exhibited an ambipolar behavior with hole dominant transport. Hole mobilities increased with increasing boiling point (bp) of the nonchloririated solvents: 0.03, 0.05, and 0.10 cm(2) V-1 s" for devices processed using TOL, XY, and TMB, respectively. Thermal annealing further improved the FET performance. TMB-based polymer FETs annealed at 200 degrees C yielded a maximum hole mobility of 1.28 cm(2) s(-1), which is far higher than the 0.43 cm(2) V-1 s(-1) obtained from the CF-based device. This enhancement was attributed to increased interchain interactions as well as improved long-range interconnection between fibrous domains. Moreover, all of the nonchlorinated solutions generated purely edge-on orientations of the polymer chains, which is highly beneficial for carrier transport in FET devices. Furthermore, we fabricated an array of flexible TMBprocessed PDPP2DT-F2T2 FETs on the plastic PEN substrates. These devices demonstrated excellent carrier mobilities and negligible degradation after 300 bending cycles. Overall, we demonstrated that the organized assembly of polymer chains can be achieved by slow drying using high bp nonchlorinated solvents and a post thermal treatment. Furthermore, we showed that polymer FETs processed using high bp nonhalogenated solvents may outperform those processed using halogenated solvents.

• 出版日期2017-8-30