摘要
Lamellar structures of Ti-46Al-0.5W-0.5Si (at-%) alloy solidifying through the primary alpha phase were successfully aligned parallel to the growth direction using a self-seeding technology in a Bridgman type directional solidification furnace. At the growth rate of 20 mu m s(-1) and temperature gradient of 12.1 K mm(-1), the alpha phase grows along the <11<(2)over bar>0> direction. Therefore, the parallel lamellar structures, whose lamellar orientation is <11<(2)over bar>0> direction, can grow continuously until the end of solidification under these solidification parameters. The original lamellar structures of the unmelted region parallel to the growth direction and suitable solidification parameters are necessary for TiAl alloys solidifying through the primary alpha phase to control the lamellar orientation. The self-seeding technology gets rid of the cutting and fixing of seeds and simplifies the processing of controlling the lamellar orientation of TiAl alloys. It can promote the engineering applications of the lamellar orientation control of TiAl alloys.