Direct observation of electron emission from grain boundaries in CVD diamond by PeakForce-controlled tunnelling atomic force microscopy

作者：Harniman Robert L^*; Fox Oliver J L; Janssen Wiebke; Drijkoningen Sien; Haenen Ken; May Paul W

来源：Carbon, 2015, 94: 386-395.

DOI：10.1016/j.carbon.2015.06.082

A detailed investigation of electron emission from a set of chemical vapour deposited (CVD) diamond films is reported using high-resolution PeakForce-controlled tunnelling atomic force microscopy (PF-TUNA). Electron field emission originates preferentially from the grain boundaries in low-conductivity polycrystalline diamond samples, and not from the top of features or sharp edges. Samples with smaller grains and more grain boundaries, such as nanocrystalline diamond, produce a higher emission current over a more uniform area than diamond samples with larger grain size. Light doping with N, B or P increases the grain conductivity, with the result that the emitting grain-boundary sites become broader as the emission begins to creep up the grain sidewalls. For heavy B doping, where the grains are now more conducting than the grain boundaries, emission comes from both the grain boundaries and the grains almost equally. Lightly P-doped diamond samples show emission from step-edges on the (111) surfaces. Emission intensity was time dependent, with the measured current dropping to similar to 10% of its initial value similar to 30 h after removal from the CVD chamber. This decrease is ascribed to the build-up of adsorbates on the surface along with an increase in the surface conductivity due to surface transfer doping.

• 出版日期2015-11