Microwave assisted hydrothermal synthesis of Au@TiO2 core-shell nanoparticles for high temperature CO sensing applications

作者：Kim Yun Su; Rai Prabhakar; Yu Yeon Tae^*

来源：Sensors and Actuators B: Chemical , 2013, 186: 633-639.

DOI：10.1016/j.snb.2013.06.038

• Au@TiO2
• Core-shell NPs
• Surface plasmon resonance
• Crystallinity
• Gas sensor
• CO gas

Au@TiO2 core-shell nanoparticles (NPs) were synthesized by microwave assisted hydrothermal method in 1 h. Au NPs with 40 +/- 5 nm size were synthesized by colloidal method. TiO2 shell layer with 60 +/- 10 nm shell thickness was deposited on Au NPs by microwave assisted hydrothermal method. The average particle size of primary TiO2 NPs was 15 +/- 3 nm. The surface plasmon (SP) band of Au NPs was red-shifted from 521 nm to 565 nm after TiO2 shell formation. There was no phase transition from anatase to rutile even these Au@TiO2 core-shell NPs were sintered at 900 degrees C. The sensor response of Au@TiO2 core-shell NPs was higher than bare TiO2 NPs. The response of Au@TiO2 core-shell NPs increased with increasing CO concentration. The response further increased with increasing testing temperature but decreased with increasing sintering temperature.

• 出版日期2013-9