Microscopic examination of a new mechanism for accelerated degradation of synthetic fibre reinforced marine concrete

作者：Hughes P^*; Fairhurst D; Sherrington I; Renevier N; Morton L H G; Robery P C; Cunningham L

来源：Construction and Building Materials, 2013, 41: 498-504.

DOI：10.1016/j.conbuildmat.2012.12.022

• Algal fronds
• Marine concrete
• Synthetic fibres
• Degradation
• Holistic model

This research presents an exploratory study into the mechanical biodeterioration of synthetic fibre reinforced marine concrete. Light and inverted microscopy, scanning electron microscopy (SEM) with energy dispersive X-ray analyser (EDX) of site specimens were used to observe colonisation at the fibre cement interface, enabling the further understanding of this interaction. Algal fronds have been observed growing between fibre and cement. Colonisation has been observed, entangled with, and adhered to fibres. This new mechanism occurs when the material bond is weakened as a direct result of the physical activity of an organism, such as its growth. Loss of surface material, either through biodeterioration or through other mechanical means, such as power washing, is not the primary cause of degradation, but may exacerbate the condition. A holistic model is presented, detailing the degradation process of macro and microsynthetic fibres. Microscopic investigation of site concrete revetment armour units was used to validate the model. This multidisciplinary study is the first to report the composition of microbial assemblages fouling and degrading synthetic fibres within marine concrete in the United Kingdom, laying the foundation for more study into this new phenomenon.

• 出版日期2013-4