Non-Destructive Analysis of Degradation Mechanisms in Cycle-Aged Graphite/LiCoO2 Batteries

作者：Zhang Liqiang; Wang Lixin; Lyu Chao^*; Li Junfu; Zheng Jun

来源：Energies, 2014, 7(10): 6282-6305.

DOI：10.3390/en7106282

• degradation mechanisms
• cycle life
• multi-physics model
• lithium-ion battery

Non-destructive analysis of degradation mechanisms can be very beneficial for the prognostics and health management (PHM) study of lithium-ion batteries. In this paper, a type of graphite/LiCoO2 battery was cycle aged at high ambient temperature, then 25 parameters of the multi-physics model were identified. Nine key parameters degraded with the cycle life, and they were treated as indicators of battery degradation. Accordingly, the degradation mechanism was discussed by using the multi-physics model and key parameters, and the reasons for capacity fade and the internal resistance increase were analyzed in detail. All evidence indicates that the formation reaction of the solid electrolyte interface (SEI) film is the main cause of battery degradation at high ambient temperature.

• 出版日期2014-10
• 单位哈尔滨工业大学