Layered double oxide (LDO) particle containing photoreactive hybrid layers with tunable superhydrophobic and photocatalytic properties

作者：Deak Agota; Janovak Laszlo; Csapo Edit; Ungor Ditta; Palinko Istvan; Puskas Sandor; Ordog Tibor; Ricza Tamas; Dekany Imre^*

来源：Applied Surface Science, 2016, 389: 294-302.

DOI：10.1016/j.apsusc.2016.07.127

• Layered double oxide (LDO)
• Fluoropolymer
• Superhydrophobic
• Photoreactive hybrid layer
• Selective wetting

Inorganic/organic hybrid layers have been prepared having superhydrophobic as well as photoreactive properties. The hybrid thin films with micro- and nanosized dual-scale surface roughness consist of similar to 25 mu m layered double oxide (LDO) photocatalyst particles and low surface energy poly(perfluorodecyl acrylate) [p(PFDAc)] fluoropolymer binder material. The application of [p(PFDAc)] resulted in the decrease in the surface free energy of the hydrophilic LDO. The structured surface LDO with similar to 12% ZnO phase content were synthesized from layer double hydroxide (LDH) spheres. The determined excitation wavelength and the calculated band gap energy values were 386 nm and 3.23 eV, respectively. The hybrid thin films were prepared by a simple spray-coating method, which is a low-cost, fast and scalable film-forming technique. The surface roughness and also the wetting properties of the two-component hybrid layers proved to be finely adjustable by the LDO:fluoropolymer ratio. It was found that at 80-90 wt% LDO content, the thin films with a surface free energy value of similar to 12 mJ/m(2) displayed superhydrophobic behaviour (Theta > 150 degrees) with satisfactory photocatalytic properties. This means special photoreactive surfaces with superhydrophobic properties instead of the conventional superhydropilic photocatalyst layers. According to the benzoic acid photodegradation test experiments of benzoic acid, the hybrid layers with 80-90 wt% LDO content photooxidized 22-24% of the initial test molecule concentration (0.17 g/L) under UV-A (lambda(max) = 365 nm) illumination.

• 出版日期2016-12-15