A novel method of synthesis and microstructural investigation of calcium titanate powders

作者：Lei, Xianjun; Xu, Baoqiang^*; Yang, Bin; Xu, Binbin; Guo, Xutao

来源：Journal of Alloys and Compounds, 2017, 690: 916-922.

DOI：10.1016/j.jallcom.2016.08.213

• Calcium titanate
• Perovskite structure
• Thermal sintering method
• Microstructure
• Calcium chloride bihydrate

A novel method, using calcium chloride bihydrate (CaCl2. 2H(2)O and TiO2) as raw materials, to synthesize crystalline calcium titanate (CaTiO3) has been investigated by thermodynamic calculation and X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), differential scanning calorimetric-thermogravimetric analysis (DSC-TG), high resolution transmission electron microscopy (HR-TEM) etc. Using XRD technique analyzed experimental results revealed success of thermal sintering process, in which the mass ratio of M CaCl2 center dot 2H(2)O/M-Tio2 = 2:1, holding temperature of 1073 K, preservation time 2 h, could be used to produce crystalline CaTiO3 powders. Ratio of Ca/Ti/O = 1:1:3 was verified by EDS pot-scan. According to SEM observation, the crystalline CaTiO3 powders are mainly composed of many separated particles with average size approximately 10 mu m and have been demonstrated a strongly faceted morphology. The lattice plane, (112) is clearly observed in the HR-TEM micrograph and the lattice distance was measured as 0.27 nm.

• 出版日期2017-1-5
• 单位昆明理工大学