A facile fabrication of n-type Bi2Te3 nanowire/graphene layer-by-layer hybrid structures and their improved thermoelectric performance

作者：Ju Hyun; Kim Myeongjin; Kim Jooheon

来源：Chemical Engineering Journal, 2015, 275: 102-112.

DOI：10.1016/j.cej.2015.04.042

• Thermoelectric
• Bi2Te3 nanowire
• Graphene
• Layer-by-layer structure

n-Type Bi2Te3 nanowire/graphene composite films were prepared with a facile wet chemical synthesis and sintering process, and the effect of Bi2Te3 nanowire content on the thermoelectric properties of the composite films were investigated. The one-dimensional Bi2Te3 nanowires were homogeneously intercalated and dispersed between the prepared graphene layers, forming the Bi2Te3 nanowire/graphene layer-by-layer hybrid structure. These composite films showed enhanced thermoelectric properties compared to the pristine graphene film fabricated with the same methods but without the Bi2Te3 nanowires. This was attributed to both the large Seebeck coefficient, which is intrinsic to the Bi2Te3 nanowires, and the reduced thermal conductivity, which is attributed to the exceptional phonon scattering at the interfaces between the nanowires and graphene layers. The maximum thermoelectric efficiency (ii) of the Bi2Te3 nanowire/graphene composites was achieved with a Bi2Te3 nanowire content of 20 wt.%. This composite had a dramatically improved ZT value of 0.2, which was 27 times larger than that of the pristine graphene film.

• 出版日期2015-9-1