Nanoparticles of Ca-Ru-O precursors have been prepared using a reverse micelle. Transmission electron microscopy and x-ray diffraction techniques showed that the precursors had an amorphous structure. The average diameter of the amorphous Ca-Ru-O particles was shown to be approximately 10 nm (within a range of /- 2 nm). An interesting result was that a rod-like nano-CaRuO(3) perovskite was observed when the precursor was sintered at a temperature of 950 degrees C. Furthermore, the conversion of the powders to crystalline CaRuO(3) perovskite occurred upon heat treatment at 450 degrees C in air. This is much lower than that for a standard solid-state reaction for CaCO(3) and RuO(2).
- 出版日期2009-2-25