An improved carbonate co-precipitation method for the preparation of spherical Li[Ni1/3Co1/3Mn1/3]O-2 cathode material

作者：Zhang S^*; Deng C; Yang S Y; Niu H

来源：Journal of Alloys and Compounds, 2009, 484(1-2): 519-523.

DOI：10.1016/j.jallcom.2009.04.149

• Electrode materials
• Co-precipitation
• X-ray diffraction
• Electrochemical reaction

An improved carbonate co-precipitation method was employed to prepare spherical Li[Ni1/3Co1/3Mn1/3]O-2 cathode material. The precursor, [Ni1/3Co1/3Mn1/3]CO3, Was prepared using ammonia as chelating agent under CO2 atmosphere. The spherical Li[Ni1/3Co1/3Mn1/3]O-2 was prepared by mixing the precalcined [Ni1/3Co1/3Mn1/3]CO3 with 7% excess LiOH followed by high-temperature calcination. Compared with the Li[Ni1/3Co1/3Mn1/3]O-2 prepared by the conventional carbonate co-precipitation method, the Li[Ni1/3Co1/3Mn1/3]O-2 prepared by the improved carbonate co-precipitation method showed larger specific surface area and better electrochemical performance. The initial discharge capacity of the Li[Ni1/3Co1/3Mn1/3]O-2 prepared by the improved carbonate co-precipitation method was 162mAhg(-1) and 96.6% of the initial discharge capacity was retained after 50 charge-discharge cycling. However, the tap density of the Li[Ni1/3Co1/3Mn1/3]O-2 Prepared by the improved carbonate co-precipitation method is lower than that of the Li[Ni1/3Co1/3Mn1/3]O-2 prepared by the conventional carbonate co-precipitation method, and the tap densities of both Li[Ni1/3Co1/3Mn1/3]O-2 samples are lower than that of the Li[Ni1/3Co1/3Mn1/3]O-2 prepared by the hydroxide co-precipitation method.

• 出版日期2009-9-18
• 单位哈尔滨工程大学; 哈尔滨师范大学