Dust-induced shading on photovoltaic modules

作者：Qasem Hassan^*; Betts Thomas R; Muellejans Harald; AlBusairi Hassan; Gottschalg Ralph

来源：Progress in Photovoltaics: Research and Applications , 2014, 22(2): 218-226.

DOI：10.1002/pip.2230

• dust
• spectral response
• amorphous silicon
• crystalline silicon
• transmittance
• soiling ratio

The effect of dust on photovoltaic modules is investigated with respect to concentration and spectral transmittance. Samples were collected in the form of raw dust as well as accumulated dust on exposed sheets of glass at different tilt angles. Spectral transmittance of the samples was determined. Transmittance variation between top, middle and bottom was identified for samples collected at different inclinations, where the worst case was seen at a tilt angle of 30(o) with a non-uniformity of 4.4% in comparison with 0.2% for the 90 degrees tilt. The measured data showed a decrease in transmittance at wavelengths %26lt;570nm. Integrating this with measured spectral responses of different technologies demonstrates that wide band-gap thin-film technologies are affected more than, for example crystalline silicon technologies. The worst case is amorphous silicon, where a 33% reduction in photocurrent is predicted for a dust concentration of 4.25mg/cm(2). Similarly, crystalline silicon and CIGS technologies are predicted to be less affected, with 28.6% and 28.5% reductions in photocurrent, respectively. The same procedure was repeated with varying Air Mass (AM), tilt angle and dust concentration values to produce a soiling ratio table for different technologies under different AM, tilt angle and dust concentration values.

• 出版日期2014-2